FMSC - RenLam 1310 / Ren 1510 Ultra High Temperature Laminating System (Black)

Back to: Home >> Liquid Tooling Materials >> Epoxy Laminating Resins >> High Temperature Laminating Resins

RenLam 1310 / Ren 1510 Ultra High Temperature Laminating System (Black)


	9,000 cps Viscosity \| 91D Shore Hardness 400 Min Gel Time

RenLam 1310 Resin / Ren 1510 Hardener is a high temperature epoxy laminating resin that features a 412°F Tg. This material is ideal for laminated tooling requiring 350°F temperature resistance with extended service life. It requires a high temperature post cure for optimum properties.

CAUTION: This product will produce high exotherm and give off acrid smoke if left to cure in thicker masses. Left over mixed resin and hardener should be spread out in a thin layer to cure.

This material replaces RenLam 1310/Ren 1520.

		View the specification table
		View the MSDS
		Video: Preparing Liquid Tooling Materials
		Video: Working with Epoxy Surface Coat and Laminating Resin

		Fiberglass Reinforcements
		Mold Releases - Sacrificial
		Mixing Cups & Paddles

Request For Quote & Ordering Information

Catalog Number	Description	UM	Net Wt.	Ship Note	Qty
056181	RenLam 1310 Resin Only 5 Gallon	EA	45
056040	Ren 1510 Hardener - 1 Gal	EA	6.75	HAZ-G

Click Here to View Closeout Specials

S&H - Freeman charges standard published UPS/FedEx shipping rates (unless freight is specified). All orders under $25 are subject to a $5 small order fee. International orders are subject to a $250 minimum order.

SO = Special Order, Minimum Quantities and Extended Lead Times May Apply.

HAZ-G = Hazardous material, cannot ship air, $20 surcharge applied for each package shipped ground.
HAZ-A = Hazardous material, cannot ship air, no surcharge for ground shipping.
HAZ-T = Toxic material, must be sent by freight carrier.
FRT = must be sent by freight carrier due to size, weight, or hazardous classification.

T = Thickness L = Length W = Width H = Height Dia = Diameter Rad = Radius.
Net Wt. = Net Weight (shipping weight may be more).