Room Temperature Surface Coats

Product
Number

Mix Ratio
(by wt.)
Resin:
Hardener

Mix Ratio
(by vol.)
Resin:
Hardener

Gel
Time
(min.)
@ 72°F

Demold
Time
(hours)
@ 72°F

Hardness
(Shore D)

Mixed
Viscosity
(cps)

Volumetric
Yield
(cu. in. / lb.)

Shrink
(in / in)

Compressive
Strength
(psi)

Flexural
Strength
(psi)

Flexural
Modulus
(psi)

Tensile
Strength
(psi)

C.T.E.
(in / in / °F) *

Deflection
Temp. (°F)

Freeman 701

100:8

100:13

15

24

87

Thixotropic

1.5

18.7

-

13,200

10,800

-

6,100

-

127

Freeman 705 - 15

100:14

4.9:1

15

24

90

18,300

1.4

19.58

-

16,800

7,000

.76 x 10⁶

5,100

-

250

Freeman 705 - 45

100:14

4.9:1

45

24

90

18,300

1.4

19.58

-

16,800

7,000

.76 x 10⁶

5,100

-

250

Freeman 706 - 45

100:14

4.9:1

45

24

90

15,000

1.3

20.97

-

16,800

7,000

.76 x 10⁶

5,100

-

250

RenGel 1118

100:9

100:13

30

24

90

Paste

1.5

19.0

0.002

13,400

6,500

-

3,500

2.56 x 10^-5

235

169

RenGel 1124

100:18

100:27

25

24

90

Paste

1.4

19.0

0.002

14,500

10,000

-

6,200

2.86 x 10^-5

127

149

RenGel 1126

100:18

100:25

24

24

90

Paste

1.4

19.7

0.002

12,000

6,800

-

4,700

2.6 x 10^-5

127

165

RenGel 1129

100:20

100:26

20

24

85

Paste

1.4

19.9

0.0016

13,800

15,500

.49 x 10⁶

4,900

3.16 x 10^-5

117

156

RenGel 3260

100:9

100:16

33

24

88

30,000

1.9

14.6

0.002

17,000

9,600

1.4 x 10⁶

6,500

2.10 x 10^-5

138

181

High Temperature Surface Coats

Product
Number

Mix Ratio
(by wt.)
Resin:
Hardener

Mix Ratio
(by vol.)
Resin:
Hardener

Gel
Time
(min.)
@ 72°F

Demold
Time
(hours)
@ 72°F

Hardness
(Shore D)

Mixed
Viscosity
(cps)

Volumetric
Yield
(cu. in. / lb.)

Shrink
(in / in)

Compressive
Strength
(psi)

Flexural
Strength
(psi)

Flexural
Modulus
(psi)

Tensile
Strength
(psi)

C.T.E.
(in / in / °F) *

Deflection
Temp. (°F)

Freeman 935 - 15

100:11

5.62:1

28

24

88

27,500

1.6

17.76

-

26,500

7,900

1.3 x 10⁶

4,000

2.3 x 10^-5

370

Freeman 935 - 30

100:11

5.62:1

43

24

90

29,500

1.6

17.31

-

26,500

7,950

1.3 x 10⁶

4,000

2.3 x 10^-5

370

Freeman 935 - 90

100:11

5.62:1

90

24

88

25,350

1.6

17.4

-

26,500

7,950

1.3 x 10⁶

4,000

2.3 x 10^-5

370

Freeman 945

100:10

100:14

50

24

90

Thixotropic

1.4

19.9

-

25,000

8,000

-

5,000

3.7 x 10^-5

310

RenGel 4026 /
Ren 1500

100:10

100:14

50-60

24

90

Paste

1.4

19.5

-

27,000

8,500

-

5,500

3.7 x 10^-5

-

310

RenGel 4026 /
Ren 1501

100:10

100:14

30-40

24

90

Paste

1.4

19.5

-

27,000

8,000

-

4,000

3.2 x 10^-5

-

310

RenGel 4026 /
Ren 1510

100:10

100:14

120-150

24

90

Paste

1.4

19.5

-

26,000

8,700

-

6,000

3.8 x 10^-5

-

335

RenGel 8026 /
Med Hard

100:10

100:14

30-40

24

90

Paste

1.4

19.4

-

27,000

8,000

-

4,000

3.2 x 10^-5

-

310

RenGel 177-144 /
Ren 1500

100:10

100:15

60

24

92

Paste

1.6

17.8

0.002

28,000

12,500

.7 x 10⁶

7,000

2.4 x10^-5

-

284

24

.49 x 10⁶

-

RenGel 188-11 /
Ren 188-10

100:10

100:14

50

24

90

Paste

1.5

19.9

-

25,000

8,000

-

5,000

3.7 x 10^-5

-

310

RenGel 1320 /
Ren 1510

100:8

100:12

240

24

93

Paste

1.5

18.5

0.003

28,500

12,300

-

8,800

1.72 x 10^-5

-

396

RenGel 1320 /
Ren 1520

100:19

-

480

24

90

Paste

1.4

19.8

0.005

20,500

8,600

-

5,000

2.05 x 10^-5

-

457

ASTM

-

-

D-2471

-

D-2240

D-2393

D-792

D-2566

D-695

D-790

D-790

D-638

D-696

D-648