Note: Product titles link to the respective product pages.
Mix Ratio
(by wt.) |
Mix Ratio
(by vol.) |
Gel Time
(min.) @ 72°F |
Demold
Time (hr.) @ 72°F |
Hardness
(Shore D) |
Mixed
Viscosity (cps) |
Density
(g/cc) |
Volumetric
(in.3/lb.) |
Compressive
Strength (psi) |
Flexural
Strength (psi) |
Flexural
Modulus (psi) |
Tensile
Strength (psi) |
C.T.E.
(in./in./°F) |
Deflection
Temp. (°F) |
Tg (°F)
|
|
Room Temperature Laminating Resins | |||||||||||||||
100:24
|
100:25
|
38
|
24
|
90
|
800
|
1.13
|
24.5
|
26,000
|
39,000
|
–
|
36,000
|
0.93 x 10-5
|
128
|
–
|
|
100:26
|
100:25
|
20
|
24
|
90
|
1,120
|
1.13
|
24.5
|
28,000
|
37,000
|
–
|
26,000
|
1.0 x 10-5
|
128
|
–
|
|
100:23
|
4:1
|
35
|
24
|
82
|
800
|
1.10
|
25.1
|
10,600
|
14,200
|
320,000
|
8,800
|
‐
|
120
|
–
|
|
100:22
|
4:1
|
15
|
24
|
84
|
900
|
1.14
|
‐
|
11,900
|
14,700
|
476,000
|
8,600
|
‐
|
140
|
–
|
|
100:10
|
100:14
|
28
|
24
|
88
|
3,000
|
1.39
|
19.9
|
39,900
|
9,100
|
–
|
25,000
|
–
|
128
|
–
|
|
100:16
|
100:20
|
20
|
24
|
82
|
2,850
|
1.30
|
21.3
|
40,000
|
33,500
|
1.8 x 106
|
25,300
|
–
|
188
|
–
|
|
100:20
|
100:26
|
37
|
24
|
86
|
2,800
|
1.28
|
21.6
|
40,000
|
33,500
|
1.8 x 106
|
25,300
|
–
|
188
|
–
|
|
100:17
|
3.5:1
|
30
|
24
|
89
|
3,000
|
1.36
|
20.3
|
48,000
|
–
|
–
|
24,400
|
–
|
135
|
–
|
|
100:33
|
100:37
|
90
|
24
|
86
|
1,445
|
1.10
|
25
|
26,500
|
39,900
|
1.3 x 106
|
35,500
|
–
|
180
|
–
|
|
100:25
|
3.5:1
|
15-20
|
24
|
82
|
700
|
1.17
|
23.6
|
27,800
|
23,500
|
451,000
|
13,900
|
–
|
140
|
–
|
|
100:26
|
100:28
|
20
|
24
|
90
|
2,000
|
1.13
|
24.5
|
28,000
|
37,000
|
1.55 x 106
|
26,000
|
1.0 x 10-5
|
128
|
–
|
|
100:23
|
100:25
|
36
|
24
|
89
|
1,350
|
1.13
|
24.5
|
24,700
|
40,700
|
1.7 x 106
|
34,900
|
0.97 x 10-5
|
129
|
–
|
|
100:16
|
100:23
|
22
|
24
|
90
|
3,500
|
1.35
|
20.5
|
23,000
|
30,000
|
1.8 x 106
|
25,000
|
1.20 x 10-5
|
129
|
164
|
|
100:16
|
100:23
|
35
|
24
|
89
|
2,000
|
1.35
|
20.5
|
26,900
|
32,900
|
1.5 x 106
|
25,000
|
0.81 x 10-5
|
–
|
–
|
|
100:15
|
100:21
|
40
|
24
|
90
|
3,200
|
1.34
|
20.5
|
21,000
|
36,000
|
1.6 x 106
|
20,000
|
1.02 x 10-5
|
–
|
164
|
|
100:24
|
–
|
38
|
24
|
90
|
800
|
1.15
|
24.1
|
26,000
|
39,000
|
–
|
36,000
|
0.93 x 10-5
|
–
|
273
|
|
100:25
|
100:29
|
35
|
24
|
92
|
2,500
|
1.13
|
18.5
|
23,450
|
42,180
|
1.91 x 106
|
32,224
|
1.2 x 10-6
|
128
|
167
|
|
High Temperature Laminating Resins
|
|||||||||||||||
100:10
|
100:13
|
52
|
24
|
92
|
4,000
|
1.46
|
19.0
|
24,500
|
30,574
|
1.6 x 106
|
23,000
|
2.25 x 10-5
|
–
|
301
|
|
100:13
|
100:18
|
60
|
24
|
90
|
3,600
|
1.31
|
21.1
|
52,800
|
33,000
|
–
|
26,000
|
1.27 x 10-5
|
–
|
300
|
|
100:14
|
6:1
|
30
|
24
|
88
|
1,800
|
1.15
|
24.0
|
21,600
|
16,600
|
470,000
|
12,400
|
2.65 x 10-5
|
355
|
–
|
|
100:14
|
100:15
|
50
|
24
|
90
|
1,900
|
1.19
|
23.3
|
28,000
|
35,000
|
1.6 x 106
|
26,000
|
0.85 x 10-5
|
289
|
338
|
|
100:11
|
100:14
|
55
|
24
|
90
|
4,000
|
1.34
|
20.8
|
28,000
|
34,000
|
1.7 x 106
|
24,000
|
1.41 x 10-5
|
–
|
333
|
|
100:15
|
100:18
|
90
|
24
|
93
|
8,000
|
1.42
|
19.6
|
44,000
|
77,000
|
4.4 x 106
|
80,000
|
3.4 x 10-6
|
–
|
350
|
|
100:38
|
100:47
|
7 hrs
|
24
|
–
|
700
|
1.17
|
20.2
|
–
|
20,305
|
4.5 x 106
|
12,473
|
–
|
–
|
273
|
|
100:19
|
‐
|
50-60
|
‐
|
90
|
2,500
|
1.09
|
25.3
|
‐
|
90,480
|
4,642
|
62,630
|
‐
|
306
|
305
|
|
100:25
|
‐
|
50-75
|
‐
|
88
|
3,500
|
1.18
|
23.4
|
‐
|
44,540
|
2,296
|
33,690
|
‐
|
320
|
331
|
|
100:24
|
‐
|
180-210
|
‐
|
90
|
4,500
|
1.14
|
24.2
|
‐
|
76,200
|
3,504
|
56,090
|
‐
|
389
|
450
|
|
ASTM
|
–
|
–
|
D-2471
|
–
|
D-2240
|
D-2393
|
D-792
|
D-792
|
D-695
|
D-790
|
D-790
|
D-638
|
D-696
|
D-648
|
D-648
|
*Properties vary based on cure schedule. See TDS for details.