Intermediate Cure Urethane Specifications
|
This table includes discontinued items and their recommended alternatives. Go back to the Current Products Only specification table. |
Mix Ratio (by wt.) |
Mix Ratio (by vol.) |
Gel Time (min.) @ 72°F |
Demold Time (hr.) @ 72°F |
Cast Thick. |
Hardness (Shore A) |
Viscosity (R/H or Mixed (cps) |
Density (g/cc) |
Volumetric Yield (in.3/lb.) |
Shrink (in./in.) |
Compressive Strength (psi) |
Flexural Strength (psi) |
Flexural Modulus (psi) |
Tensile Strength (psi) |
Deflection Temp (°F) |
Izod Impact (ft.lb./in.) |
Tg per DMA (°F) |
Cured Color |
|
RenCast 6486 (Disc. June 2022) No direct alternative |
100:50 |
1:1 |
7-8 |
8 hr. |
1/8" |
67 |
7,800/75 |
1.16 |
23.9 |
– |
– |
4,750 |
110,000 |
3,600 |
156 |
6.6 |
156 |
Amber |
Freeman 1085 (Disc. June 2022) Replaced by Freeman 1085HS |
1:1 |
1:1 |
6 |
30-120 min. |
3" |
69 |
80 |
1.12 |
24.7 |
0.002 |
4,880 |
5,600 |
170,000 |
3,300 |
137 |
0.35 |
172 |
Beige |
1:1 |
1:1 |
7 |
30 min. |
3" |
70 |
90 |
1.05 |
26.6 |
0.003 |
‐ |
4,500 |
235,000 |
4,500 |
‐ |
3.0 |
‐ |
White |
|
RenCast 6497 (Disc. June 2022) No direct alternative |
1:1 |
– |
4-5 |
2 hr. |
1/8" |
70 |
1,875 |
1.1 |
25.2 |
– |
– |
– |
– |
995 |
– |
– |
– |
Light Amber |
100:92 |
1:1 |
3 |
15-30 min. |
1/2" |
70 |
80 |
1.05 |
26.6 |
0.010 |
3,650 |
4,500 |
132,000 |
3,000 |
140 |
– |
– |
Off White |
|
115:100 |
1:1 |
20 |
2-4 hr. |
1/2" |
80 |
150 |
1.12 |
24.7 |
0.003 |
8,300 |
9,500 |
288,000 |
6,650 |
134 |
0.31 |
– |
White |
|
1:1 |
1:1 |
20 |
2-4 hr. |
3" |
75 |
190 |
1.09 |
25.4 |
0.001 |
‐ |
9,000 |
‐ |
5,400 |
140 |
1.32 |
‐ |
White |
|
|
ASTM |
– |
– |
D-2471 |
– |
– |
D-2240 |
D-2393 |
D-792 |
D-792 |
D-2566 |
D-695 |
D-790 |
D-638 |
D-790 |
D-648 |
D-256 |
D-4065 |
– |
*Deflection Temperature is the temperature when a 1/2" x 1/2" x 5" bar (supported at both ends) deflects 0.010 of an inch under a 66 psi fiber stress. The maximum service temperature may be far above this value depending on the application and the stress of the plastic at high temperature.
 |
For comparison, you may also want to check out: | |
 |
Rapid Cure Urethane Elastomers | |
|
Overnight Cure Urethane Elastomers - Flexible | |
|
Overnight Cure Urethane Elastomers - Semi-Rigid | |
|
Overnight Cure Urethane Elastomers - Rigid | |