Note: All product titles link to the respective product pages.
|
Hardness
Shore D |
Density
g/cc |
Density
lb./ft.3 |
Tensile
Strength (psi) |
Compressive
Strength (psi) |
Compressive
Modulus Elasticity (psi) |
Flexural
Strength (psi) |
Flexural
Modulus (psi) |
Glass
Transition Temp (°F) |
Coefficient
Thermal Expansion (in./in./°F) |
Color
|
54
|
0.55
|
34
|
1,300
|
1,400
|
105,000
|
2,300
|
106,000
|
203
|
34.4 x 10-6
|
Red Brown
|
|
60
|
0.60
|
37
|
1,300
|
2,900
|
101,526
|
2,900
|
106,000
|
203
|
30.5 x 10-6
|
Lt. Brown
|
|
65
|
0.66
|
41
|
2,300
|
2,800
|
135,000
|
4,000
|
144,000
|
205
|
36.0 x 10-6
|
Lt. Brown
|
|
60
|
0.67
|
42
|
1,570
|
3,600
|
139,104
|
4,340
|
125,770
|
185
|
27.7 x 10-6
|
Lt. Brown
|
|
60
|
0.70
|
43
|
1,886
|
3,625
|
139,236
|
4,351
|
152,000
|
187
|
30.5 x 10-6
|
Lt. Brown
|
|
64
|
0.77
|
48
|
1,800
|
2,200
|
181,000
|
3,700
|
185,000
|
219
|
29.9 x 10-6
|
Lt. Brown
|
|
59
|
0.59
|
37
|
2,538
|
2,538
|
–
|
3,263
|
–
|
221
|
31 x 10-6
|
Brown
|
|
62
|
0.64
|
40
|
3,989
|
3,989
|
–
|
3,989
|
–
|
225
|
31 x 10-6
|
Brown
|
|
69
|
0.72
|
44
|
4,714
|
4,714
|
–
|
3,989
|
–
|
–
|
26 x 10-6
|
Lt. Brown
|
|
71
|
0.72
|
45
|
5,076
|
5,076
|
–
|
4,360
|
–
|
230
|
27 x 10-6
|
Lt. Brown
|
|
68
|
0.74
|
46.5
|
3,762
|
–
|
–
|
5,150
|
154,200
|
–
|
46.8 x 10-6
|
Brown
|
|
71
|
0.75
|
46.8
|
5,000
|
5,000
|
–
|
5,438
|
–
|
230
|
31 x 10-6
|
Turquoise
|
|
ASTM
|
D-2240
|
D-792
|
D-792
|
D-638
|
D-695
|
D-695
|
D-790
|
D-790
|
D-4065
|
D-3386
|
–
|
= Ideal
= Acceptable
= Not recommended
CNC Proofing |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
Models (Architectural, styling, temporary) |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
Low-density Substructure |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
Tooling Aids & Fixtures |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
Intermediate-Temp Master & Lay-up Tools |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
High-temp master & lay-up tools |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
Foundry Patterns |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
Vacuum-Form Molds |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
Metalforming Tools |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
|
|
|
Notes
|
||||||||||||||
Adhesives
|
|||||||||||||||
X
|
X
|
X
|
X
|
X
|
X
|
X
|
X |
X
|
X
|
X
|
X
|
Low-density polyurethane with good bond strength
|
|||
X |
X |
X |
X |
X |
X |
X |
X |
X |
X |
X |
X |
Economical 5-minute epoxy |
|||
X |
X |
X |
X |
X |
X |
X |
X |
X |
X |
X |
X |
Epoxy offering longer gel times with short light handling time
|
|||
X |
X |
X |
X |
X |
X |
X |
X |
X |
X |
X |
X |
Low-viscosity epoxy laminating resin with excellent bond strength |
|||
X |
X |
X |
X |
X |
X |
X |
X |
X |
X |
X |
X |
Low-viscosity epoxy with excellent vibration and impact resistance
|
|||
Repair Materials
|
|||||||||||||||
X |
X |
X |
X |
X |
X |
X |
X |
X |
X |
X |
X |
Easy to machine polyester repair paste
|
Mix Ratio
by weight |
Viscosity (cps) |
Gel Time @ 77°F (min) |
Light Handling Time (hr) |
Hardness (Shore D) |
Density |
Service Temp. |
Color |
|
Adhesives |
||||||||
1:1 |
1,500 |
6-8 |
4 |
68 |
0.9 |
132°F |
Brown |
|
1:1
|
10,000
|
5
|
0.5
|
85
|
1.11
|
200°F
|
Clear
|
|
1:1
|
14,000
|
15-20
|
4
|
80
|
1.15
|
200°F
|
Clear
|
|
100:33
|
1,445
|
90
|
24
|
86
|
1.10
|
150°F
|
Clear
|
|
1:1
|
6,000
|
20-30
|
8
|
70
|
1.15
|
300°F
|
Clear
|
|
Repair Materials
|
||||||||
100:1.5
|
581,000
|
10
|
0.5
|
71
|
1.14
|
128°F
|
4 options
|